| Material | Boiling Point | Melting Point | Relative Density | Coefficient of Expansion |
|---|---|---|---|---|
| Units | °C | °C | gm per ml | linear per °C |
| air | . | . | 0.001293 | . |
| alcohol - ethyl | 78 | . | 0.807 | . |
| alcohol - meths | . | . | 0.823 | . |
| alcohol - proof | . | . | 0.916 | . |
| aluminum | . | . | 2.7 | 0.0000222 |
| ammonia | -33.50 | . | . | . |
| . | . | . | . | . |
| Material | Boiling Point | Melting Point | Relative Density | Coefficient of Expansion |
| Units | °C | °C | gm per ml | linear per °C |
| beeswax | . | 61.8 | . | . |
| benzene - ave | 81.5 | . | 0.899 | . |
| bismuth | 1560 | 271.3 | . | . |
| brass | . | . | . | 0.0000187 |
| brine 10% | . | . | 1.072 | . |
| brine 20% | . | . | 1.15 | . |
| bronze | . | . | 8.8 | . |
| butter - ave | . | 30.0 | . | . |
| . | . | . | . | . |
| Material | Boiling Point | Melting Point | Relative Density | Coefficient of Expansion |
| Units | °C | °C | gm per ml | linear per °C |
| cadmium | 765 | 320.9 | . | . |
| carbon dioxide | -78.5 | -56.6 (@ ≥ 5.185 bar) | 0.001977 (as a gas) | . |
| copper | 2582 | 1083.4 | . | 0.0000168 |
| copper - cast | . | . | 8.8 | . |
| copper - drawn | . | . | 8.94 | . |
| diesel | . | . | 0.853 | . |
| dry ice | . | -78.0 | 1.562 | . |
| ether | . | . | 0.736 | . |
| . | . | . | . | . |
| Material | Boiling Point | Melting Point | Relative Density | Coefficient of Expansion |
| Units | °C | °C | gm per ml | linear per °C |
| German silver | . | . | 8.6 | . |
| glass - common | . | . | 2.5 | . |
| glass - tubing | . | . | . | 0.0000083 |
| glycerine | . | . | 1.26 | . |
| gold | 2807 | 1064.4 | 19.3 | . |
| graphite | . | . | 2.5 | . |
| gunmetal | . | . | 8.2 | . |
| helium | -268.93 | -272.2 | . | . |
| hydrogen | -252.87 | -259.1 | 0.0000899 | . |
| hydrogen peroxide | 151.4 | -0.9 | . | . |
| . | . | . | . | . |
| Material | Boiling Point | Melting Point | Relative Density | Coefficient of Expansion |
| Units | °C | °C | gm per ml | linear per °C |
| ice | . | 0.0 | 0.917 | 0.000051 |
| iron | 2750 | 1535 | 7.5 | 0.0000109 |
| iron - wrought | . | . | 7.85 | 0.0000114 |
| lead | 1740 | 327.5 | 11.36 | 0.0000271 |
| magnesium | . | . | 1.74 | . |
| mercury | 356.58 | -38.9 | 13.596 | . |
| nickel | 2840 | 1450 | 8.8 | . |
| nitrogen | -195.8 | -209.9 | 0.001251 | . |
| oil - castor | . | . | 0.969 | . |
| oxygen | -183 | -214.4 | 0.001429 | . |
| ozone | -111.9 | -192.7 | . | . |
| Material | Boiling Point | Melting Point | Relative Density | Coefficient of Expansion |
| Units | °C | °C | gm per ml | linear per °C |
| paraffin | . | . | 0.89 | . |
| paraffin wax - ave | . | 52.0 | . | |
| petrol | . | . | 0.873 | . |
| pitch | . | . | 1.07 | . |
| platinum | 3800 | 1772 | 21.37 | 0.000009 |
| quartz | . | . | 2.65 | . |
| sand - silver | . | . | 2.63 | . |
| silver | 2212 | 961.9 | . | 0.0000192 |
| slate | . | . | 3.1 | . |
| solder (77.8% lead - 22.2% tin) | . | 176.5 | . | . |
| steam 100°C | . | . | 0.000598 | . |
| Material | Boiling Point | Melting Point | Relative Density | Coefficient of Expansion |
| Units | °C | °C | gm per ml | linear per °C |
| sulphur | 444.67 | 112.8 | . | . |
| sulphuric acid 15% | . | . | 1.102 | . |
| sulphuric acid 98% | 338 | . | 1.836 | . |
| tin | 2625 | 231.9 | 7.29 | . |
| tungsten | 5530 | 3410 | 19.3 | 0.0000043 |
| turpentine | 159 | . | 0.873 | . |
| water | 100 | 0.0 | 1.00 @ 4°C | . |
| water 15°C | . | . | 0.9991 | . |
| water - sea | 1.0275 | . | ||
| Wood's alloy - eutectic | . | 70 ave | . | . |
| zinc | 907 | 419.6 | 7.1 | 0.0000292 |
| . | . | . | . | . |